 note = {A study was made of wall tile bodies consisting of 80 parts of iron-free refined
SHIRASU, 10 parts of white clay, and 10 parts of white portland cement. These ingredients are mixed by dry method throughly and after drying they are pressed at 500kg/cm^2 in steel mould and heated at 1000°C in the electric muffle furnace. After cooling they are sprayed with glazes consisting of 30~60 parts of iron-free refined SHIRASU, 30~60 parts of alkaline frit, 10~20 parts of boric acid, 5~10 parts of white kaolin from IRIKI, and 5~10 parts of wollastonite from KIURA. These glazed wall tile bodies are matured at 1160°C in the electric furnace. Physical and thermal properties and bending strength of those wall tiles were investigated. Results are as follows ; apparent specific gravity 2.5~2.6, bulk specific gravity 1.8~4.9, apparent porosity 20~29%, water absorption 10~15%, and bending strength 140~186kg/cm^2.},
 pages = {5--8},
 title = {シラスの工業的利用に関する研究(第9報) : シラスを原料とする壁タイル(その1)},
 volume = {12},
 year = {1970}
}