@article{oai:ir.kagoshima-u.ac.jp:00010503,
 author = {岡村, 俊一 and OKAMURA, Shunichi and 浜崎, 美智子 and HAMASAKI, Michiko},
 journal = {鹿児島大学工学部研究報告, The research reports of the Faculty of Engineering, Kagoshima University},
 month = {Sep},
 note = {Studied on the high temperature phenomenon and corrosion of type 409 Ti-Cr stainless steel and obtained the following results : The most optimum treatment of type 409 Ti-Cr stainless steel which would not show fine precipitations in the matrix and would sustain the suitable mechanical properties of plastic deformation, is to heat-treat at 350°C for 30 min after 760°Cx30 min annealing. The corrosive ratio for hydrochloric acid and perchloric acid is very large, but it has very highly corrosion resistant for nitric acid, acetic acid, 20% aqueous solution of sodum chloride, 20% aqueous solution of sodum hydroxide, 20% aqueous solution of potassium hydroxide and ammoniak wasser.},
 pages = {27--45},
 title = {Ti-Cr Stainless steel冷延板の高温および低, 中温域に於ける熱的挙動と耐蝕性に関する研究},
 volume = {12},
 year = {1970}
}