 note = {An experimental study was carried out to obtain monodisperse polymer microspheres of 10 μm by dispersion polymerization. The microspheres of polystyrene and styrene-n-butyl acrylate copolymer were prepared. Mixtures of ethanol and ethylene glycol monomethyl ether (MeCell) were used as the
solvent. The average and variance of the particle diameters decreased by decreasing the concentration of MeCell in the solvent. The solubility of the polymer in the solvent becomes poor with a decrease in
the MeCell concentration. Monodisperse microspheres were obtained at lower temperatures than 70°C. The average particle diameters were affected by the revolution rate. In the copolymerization of
styrene and n-butyl acrylate, the conversion curve of n-butyl acrylate showed a particular tendency.},