@article{oai:ir.kagoshima-u.ac.jp:00006799,
 author = {高橋, 武重 and Takahashi, Takeshige and 原田, 佳子 and Harada, Yoshiko and 植木, 勝 and Ueki, Masaru and 甲斐, 敬美 and Kai, Takami},
 issue = {1},
 journal = {Journal of the Japan Petroleum Institute},
 month = {},
 note = {To clarify the effect of sulfur compound addition on catalytic activity and catalyst deactivation, hydrodesulfur ization (HDS) of coker gas oil (CGO) was carried out over demetallation catalysts, metal tolerant desulfurization catalyst and desulfurization catalysts. The initial HDS constant and catalyst life were slightly improved by the addition of 1 000 ppm of dimethyldisulfide (DMDS), probably by the prevention of coking on the catalyst surface. The CH3S radical formed via thermal decomposition was important in the suppression of recombination of heavy hydrocarbon radicals which results in coke or coke precursor formation. The addition of small amounts of sulfur compounds to the CGO is expected to reduce coke formation during the early stages of HDS., 数種類の水素化脱メタル触媒，耐メタル水素化脱硫触媒および水素化脱硫触媒を用いて，1.88 wt％の硫黄を含む熱分解重質軽油（CGO）の脱硫反応を高圧撹拌槽型反応器で行い，触媒の初期反応速度および活性劣化に及ぼすジメチルジスルフィド（DMDS）の添加の効果について検討した。さらに，使用済み触媒の表面積および堆積したコーク量の測定を行った。その結果，1000 ppm程度のDMDSの添加により，反応開始後24 hまでの初期反応速度が3％程度大きくなり，また活性劣化因子は最大10％程度小さくなった。DMDSの添加により，触媒表面上に堆積するコーク量が減少したことが触媒活性の向上に寄与したと考えられる。すなわち，添加したDMDSの熱分解で発生したCH3S・ラジカルが原料油の分解で生成する炭化水素ラジカルと優先的に反応して，コークあるいはその前駆体の生成を抑制したものと考えられる。このように，微量のDMDSを添加することにより，触媒の活性劣化が抑制できると考えられる。},
 pages = {22--27},
 title = {熱分解重質軽油の脱硫に及ぼす硫黄化合物添加の影響},
 volume = {49},
 year = {2005}
}