@article{oai:ir.kagoshima-u.ac.jp:00007599,
 author = {島田, 欣二 and SHIMADA, Kinji and 久米, 国幹 and KUME, Kunimoto and 福重, 安雄 and FUKUSHIGE, Yasuo},
 journal = {鹿児島大学工学部研究報告, The research reports of the Faculty of Engineering, Kagoshima University},
 month = {Mar},
 note = {Shirasu, is distributed chiefly in southern Kyushu and consists of volcanic ash, pumice and other materials. Shirasu, fly ash and slaked lime were used as raw materials as autoclave-hardened bodies. 
The press molded and then autoclaved bodies were prepared as follow; mixing ratio of slaked lime:shirasu:fly ash=1:0.85:0.15, 1:2.55:0.45, 1:5.1:0.9, mixing water (added  0-2.25% Al(H_2PO_4)_3 of all raw materials) 15%, press-molding pressure 200kg/cm^2, curing pressure 5-15kg/cm^2, curing time 5-15 hours. Results are as follow; apparent density 1.80-1.92, bulk density 1.44-1.68, water absorption 12.5-29.0%, compressive strength 108-577kg/cm^2. From the point of economic view, the best steam-curing conditions of the press molded and then autoclaved bodies are as follow; mixing ratio of slaked lime:shirasu:fly ash=1:3, mixing water 15%, addition of aluminium phosphate to mixing water 0.075%, curing pressure 10kg/cm^2, curing time 10 hours.},
 pages = {29--37},
 title = {シラスの工業的利用に関する研究 (第2報) : シラスおよびフライアッシュを用いたオートクレーブ硬化体},
 volume = {7},
 year = {1967}
}